Double Side LiFePO4 (LFP) Coated Aluminum Foil for Battery Cathode (20 m L x 200mm W x 90 um T), 1 Roll, - CAl-R-LFP

Double Side LiFePO4 (LFP) Coated Aluminum Foil for Battery Cathode (20 m L x 200mm W x 90 um T), 1 Roll, - CAl-R-LFP

Double Side LiFePO4 (LFP) Coated Aluminum Foil for Battery Cathode (20 m L x 200mm W x 90 um T), 1 Roll, - CAl-R-LFP

The graphite-coated copper foil in a roll can be used as anode for pouch cell testing.

SPECIFICATIONS

Graphite coating

Coating Thickness: ~117.4 um (double side coated)
Total Thickness: 133.4 um
Foil Thickness: 16 um
Width: 200mm (coating width of 175 mm, left and right-hand side is 12.5 mm without coating), Length: 20 m/roll
Double sides material density: 27.0±0.4 mg/cm2
Compaction density: 2.3 g/cm3
Active Material Proportion in Powder: 95.4% (PVDF and Super P is 2% and 2.6%, respectively)

Specific Capacity

150 mAh/g (Area Capacity: 3.864 mAh/cm2); 0.1 C; 2.5-3.7 V; Electrolyte: 1.0M LiPF6 in EC:DMC:EMC=1:1:1 Vol% with 1.0%VC

Charging and Discharging Curve for the First Cycle
Rate Testing
Cycling Test

$1,490.00

Double Side LiFePO4 (LFP) Coated Aluminum Foil for Battery Cathode (20 m L x 200mm W x 90 um T), 1 Roll, - CAl-R-LFP—

$1,490.00

Double Side LiFePO4 (LFP) Coated Aluminum Foil for Battery Cathode (20 m L x 200mm W x 90 um T), 1 Roll, - CAl-R-LFP

The graphite-coated copper foil in a roll can be used as anode for pouch cell testing.

SPECIFICATIONS

Graphite coating

Coating Thickness: ~117.4 um (double side coated)
Total Thickness: 133.4 um
Foil Thickness: 16 um
Width: 200mm (coating width of 175 mm, left and right-hand side is 12.5 mm without coating), Length: 20 m/roll
Double sides material density: 27.0±0.4 mg/cm2
Compaction density: 2.3 g/cm3
Active Material Proportion in Powder: 95.4% (PVDF and Super P is 2% and 2.6%, respectively)

Specific Capacity

150 mAh/g (Area Capacity: 3.864 mAh/cm2); 0.1 C; 2.5-3.7 V; Electrolyte: 1.0M LiPF6 in EC:DMC:EMC=1:1:1 Vol% with 1.0%VC

Charging and Discharging Curve for the First Cycle
Rate Testing
Cycling Test

Product Information

Shipping & Returns

Description

The graphite-coated copper foil in a roll can be used as anode for pouch cell testing.

SPECIFICATIONS

Graphite coating

Coating Thickness: ~117.4 um (double side coated)
Total Thickness: 133.4 um
Foil Thickness: 16 um
Width: 200mm (coating width of 175 mm, left and right-hand side is 12.5 mm without coating), Length: 20 m/roll
Double sides material density: 27.0±0.4 mg/cm2
Compaction density: 2.3 g/cm3
Active Material Proportion in Powder: 95.4% (PVDF and Super P is 2% and 2.6%, respectively)

Specific Capacity

150 mAh/g (Area Capacity: 3.864 mAh/cm2); 0.1 C; 2.5-3.7 V; Electrolyte: 1.0M LiPF6 in EC:DMC:EMC=1:1:1 Vol% with 1.0%VC

Charging and Discharging Curve for the First Cycle
Rate Testing
Cycling Test

You may also like

-65%NEW

PTFE Guide Sleeve and Spacer w/ optional size 10, 12, 15, 19, 20, 24mm for MTI's Split Cell- EQ-STC-SPTFE

$199.00

$69.65

-65%NEW

Split Flat Cell O-Ring Set - EQ-STC-RS

$9.99

$3.50

NEW

Mica Spacers: 50mm OD x 1mm Thick - MICA-SPACERS

$4.95

-65%NEW

Split Cell O-Ring Set - EQ-PSC-RS

$9.99

$3.50

-65%NEW

PTFE Guide Sleeves for MTI's Three-Electrode Split Test Cell - EQ-3ESTC-PS

$99.90

$34.96

-65%NEW

NaPF6 Powder for Sodium-Ion Battery Electrolyte-20g/bottle, SIB-NPF

$339.86

$118.95

NEW

PEEK Sleeves for STC-AIR-1 Split Test Cell - LAir1-PSlv

$189.00

NEW

Indium (In) Foil Sheet: 100 mm (W) x 100 mm (L) x 0.1 mm (T) - MF-In10010001

$249.00

NEW

Precision Thickness Checker For Battery Volume Expansion Measurement - PTC-TEM-LD

$3,598.00

-65%NEW

Vanadium Foil (V) Foil: L100 mm x W50 mm x T0.25 mm - MF-V-Foil-100L-0.25T

$398.00

$139.30

-65%NEW

Titanium (Ti) Foil: 110mm Width x 700 mm Length x 0.1mm Thick for Aqueous Battery Current Collector- MF-Ti700L105

$99.00

$34.65

-65%NEW

Zr - Polycrystalline Metallic Foil: 0.08mm thick x 200mm Width x 400 mm Length - MF-Zr-Foil-08Th

$698.00

$244.30